Polyurethane foam-supported double metal cyanide catalysts for polyol synthesis

ABSTRACT

Polyurethane foam-supported double metal cyanide (DMC) compounds are disclosed as useful catalysts for epoxide polymerization. The catalysts are easy to prepare, and are more active and show reduced induction periods compared with conventional powdered DMC catalysts. The catalysts of the invention can be recovered from the epoxide polymer products and can be reused to catalyze additional epoxide polymerizations.

FIELD OF THE INVENTION

The invention relates to catalysts useful for epoxide polymerization. In particular, the invention relates to double metal cyanide (DMC) compounds that are supported on a polyurethane foam. The catalysts are especially useful for preparing polyether polyols having low unsaturation.

BACKGROUND OF THE INVENTION

Double metal cyanide compounds are well known catalysts for epoxide polymerization. The catalysts are highly active, and give polyether polyols that have low unsaturation compared with similar polyols made using conventional base catalysis. Conventional DMC catalysts are prepared by reacting aqueous solutions of metal salts and metal cyanide salts to form a precipitate of the DMC compound. The catalysts can be used to make a variety of polymer products including polyether, polyester, and polyetherester polyols. Many of the polyols are useful in various polyurethane coatings, elastomers, sealants, foams, and adhesives.

Conventional double metal cyanide catalysts are usually prepared in the presence of a low molecular weight complexing ether such as glyme. The ether complexes with the DMC compound, and favorably impacts the activity of the catalyst for epoxide polymerization. In one conventional preparation, aqueous solutions of zinc chloride (excess) and potassium hexacyanocobaltate are combined. The resulting precipitate of zinc hexacyanocobaltate is combined with aqueous glyme (dimethoxyethane). An active catalyst is obtained that has the formula:

    Zn.sub.3 [Co(CN).sub.6 ].sub.2 ·xZnCl.sub.2 ·yH.sub.2 O·zGlyme

One drawback of conventional DMC catalysts is that they become finely dispersed or practically soluble in polyether polyol mixtures during epoxide polymerizations. Removal of the catalyst from the polyol following polymerization is desirable because the catalyst residues promote an undesirable accumulation of volatile materials (such as propionaldehyde) in the polyol during storage. Unfortunately, DMC catalyst residues are often difficult to remove completely from the polyols, and common catalyst removal techniques usually deactivate DMC catalysts.

Double metal cyanide catalysts usually have good activity for epoxide polymerizations. However, because the catalysts are rather expensive, catalysts with improved activity are desirable because reduced catalyst levels could be used.

Finally, DMC catalysts normally require an "induction" period. In contrast to basic catalysts, DMC catalysts ordinarily will not begin polymerizing epoxides immediately following exposure of epoxide and starter polyol to the catalyst. Instead, the catalyst needs to be activated with a small proportion of epoxide before it becomes safe to begin continuously adding the remaining epoxide. Induction periods of an hour or more are typical yet costly in terms of increased cycle time in a polyol production facility. Reduction or elimination of the induction period is desirable.

Improved DMC catalysts are needed. Catalysts having higher activity are desirable for improving productivity and reducing process cost. Double metal cyanide catalysts with shorter induction periods in epoxide polymerizations would permit a safer, more productive process. Preferred catalysts could be isolated from the polyether polyol product following synthesis and could be reused for additional polymerizations.

SUMMARY OF THE INVENTION

The invention is an epoxide polymerization catalyst. The catalyst comprises a polyurethane foam-supported double metal cyanide (DMC) compound. Surprisingly, the DMC compound remains active toward epoxide polymerization even after formulation into a polyurethane foam. In fact, the polyurethane foam-supported catalysts of the invention have superior activities and show reduced induction periods compared with conventional powdered DMC catalysts.

The invention includes a process for making the polyurethane foam-supported catalyst. The process comprises preparing a polyurethane foam from a polyol, a polyisocyanate, water, a surfactant, a foaming catalyst, and a DMC compound. The foam is easily prepared according to methods already well known in the art, except that a DMC compound is included in the foam formulation. The resulting polyurethane foam, which contains a supported DMC compound, is useful as an epoxide polymerization catalyst.

The invention also includes a process for making a polyether polyol. This process comprises polymerizing an epoxide in the presence of the polyurethane foam-supported DMC compound. Polyether polyols made with the catalysts of the invention contain unusually low levels of low molecular weight polyol impurities.

The foam-supported catalysts of the invention are easily prepared and have superior activity for epoxide polymerizations. In addition, the foam-supported catalyst of the invention can be isolated from the polyether polyol product following polyol synthesis, and can be reused as a catalyst for another epoxide polymerization.

DETAILED DESCRIPTION OF THE INVENTION

The catalyst of the invention comprises a polyurethane foam-supported double metal cyanide compound. Suitable DMC compounds are well known in the art. The preparation of DMC compounds is fully described in many references, including U.S. Pat. Nos. 5,158,922, 4,843,054, 4,477,589, 3,427,335, 3,427,334, 3,427,256, 3,278,457, and 3,941,849. The teachings of these references related to catalyst preparation and suitable DMC compounds are incorporated herein by reference in their entirety.

Generally, the DMC compounds are the reaction products of a water-soluble metal salt and a water-soluble metal cyanide salt. The water-soluble metal salt preferably has the general formula M(X)_(n) in which M is selected from the group consisting of Zn(II), Fe(II), Ni(II), Mn(II), Co(II), Sn(II), Pb(II), Fe(III), Mo(IV), Mo(VI), Al(III), V(V), V(IV), Sr(II), W(IV), W(VI), Cu(II), and Cr(III). More preferably, M is selected from the group consisting of Zn(II), Fe(II), Co(II), and Ni(II). In the formula, X is preferably an anion selected from the group consisting of halide, hydroxide, sulfate, carbonate, cyanide, oxalate, thiocyanate, isocyanate, isothiocyanate, carboxylate, and nitrate. The value of n is from 1 to 3 and satisfies the valency state of M. Examples of suitable metal salts include, but are not limited to, zinc chloride, zinc bromide, zinc acetate, zinc acetonylacetate, zinc benzoate, zinc nitrate, iron(II) sulfate, iron(II) bromide, cobalt(II) chloride, cobalt(II) thiocyanate, nickel(II) formate, nickel(II) nitrate, and the like, and mixtures thereof.

The water-soluble metal cyanide salts used to make the DMC compounds useful in the invention preferably have the general formula (Y)_(a) M'(CN)_(b) (A)_(c) in which M' is selected from the group consisting of Fe(II), Fe(III), Co(II), Co(III), Cr(II), Cr(III), Mn(II), Mn(III), Ir(III), Ni(II), Rh(III), Ru(II), V(IV), and V(V). More preferably, M' is selected from the group consisting of Co(II), Co(Ill), Fe(II), Fe(III), Cr(III), Ir(III), and Ni(II). The water-soluble metal cyanide salt can contain one or more of these metals. In the formula, Y is an alkali metal ion or alkaline earth metal ion. A is an anion selected from the group consisting of halide, hydroxide, sulfate, carbonate, cyanide, oxalate, thiocyanate, isocyanate, isothiocyanate, carboxylate, and nitrate. Both a and b are integers greater than or equal to 1; the sum of the charges of a, b, and c balances the charge of M'. Suitable water-soluble metal cyanide salts include, but are not limited to, potassium hexacyanocobaltate(III), potassium hexacyanoferrate(II), potassium hexacyanoferrate(III), calcium hexacyanocobaltate(III), lithium hexacyanoiridate(III), and the like.

The water-soluble metal salt and the water-soluble metal cyanide salt are combined in aqueous media according to methods well known in the art to produce a water-insoluble precipitate of a DMC compound. For example, when aqueous solutions of zinc chloride and potassium hexacyanocobaltate are combined at room temperature, an insoluble precipitate of zinc hexacyanocobaltate immediately forms. Usually, an excess amount of the water-soluble metal salt is used compared with the amount of water-soluble metal cyanide salt because doing so gives a catalyst with high polymerization activity.

Examples of DMC compounds that can be supported on polyurethane foam to make the compositions of the invention include, for example, zinc hexacyanocobaltate(III), zinc hexacyanoferrate(III), zinc hexacyanoferrate(II), nickel(II) hexacyanoferrate(II), cobalt(II) hexacyanocobaltate(III), and the like. Further examples of suitable DMC compounds are listed in U.S. Pat. No. 5,158,922, the teachings of which are incorporated herein by reference.

Double metal cyanide compounds are normally further activated by combining them, either during preparation or following precipitation of the catalyst, with an excess amount of a water-soluble heteroatom-containing organic liquid compound that can complex with the DMC compound, as fully described in U.S. Pat. No. 5,158,922. Suitable heteroatom-containing organic liquids include, but are not limited to, alcohols, aldehydes, ketones, ethers, esters, amides, ureas, nitriles, sulfides, and mixtures thereof. Particularly active catalysts are obtained when low molecular weight complexing ethers such as glyme are used.

The invention includes a simple process for making the foam-supported catalysts of the invention. The process comprises preparing a polyurethane foam from a polyol, a polyisocyanate, water, a surfactant, a foaming catalyst, and a DMC compound. Preferably, both an amine catalyst and an organometallic catalyst such as an organotin compound are included as foaming catalysts in the formulation. Any known process for making polyurethane foams can be used, including the one-shot and the prepolymer methods so well known to those skilled in the art of polyurethane foam manufacture. It is convenient to just slurry the DMC compound with the polyol ("B-side") components, and to combine the A-side and B-side reactants in a one-shot foaming process. Surprisingly, the normally sensitive foaming process is not adversely affected by the presence of a substantial amount of DMC compound. Also surprisingly, the DMC compound remains active toward epoxide polymerization.

When a powdered DMC compound is formulated into a polyurethane foam as described above, the resulting foam-supported catalyst typically exhibits a reduced induction period in epoxide polymerizations compared with the unsupported, powdered catalyst.

In one embodiment of the invention, an activated catalyst that requires no induction period is made. In this process, a DMC compound is combined with an epoxide and a hydroxyl group-containing starter at a temperature and for a time effective to initiate polymerization of the epoxide, but the DMC catalyst is isolated from the starter and any unreacted epoxide as soon as catalyst activation has occurred. The isolated, activated DMC catalyst is then formulated into a polyurethane foam with a polyisocyanate, water, and polyol(s) in the presence of a surfactant and a foaming catalyst.

In a second embodiment for making an activated catalyst, a DMC compound is combined with an epoxide and a hydroxyl group-containing starter at a temperature and for a time effective to initiate polymerization of the epoxide and produce an activated DMC compound/starter mixture. A polyurethane foam is then prepared by reacting a polyisocyanate, water, the activated DMC compound/starter mixture, and optional polyol(s) in the presence of a surfactant and a foaming catalyst. The resulting product is an activated, polyurethane foam-supported DMC catalyst that can be used to polymerize epoxides without an induction period.

The main advantage of the first embodiment is that it allows the manufacturer to choose a hydroxyl group-containing starter that rapidly gives an activated catalyst (1-octanol, for example), while different polyols that are more useful for foam formulation can be used to make the foam. An advantage of the second embodiment is that catalyst activation and foam formulation are performed without including a step to isolate the activated catalyst from the starter.

Generally, the hydroxyl group-containing starter can have from 1 to 8 hydroxyl groups, and can be any desired molecular weight. Any desired amount of epoxide can be reacted with the starter, provided that catalyst activation has been achieved. Catalyst activation is typically verified by an accelerated drop in reactor pressure following combination of the epoxide and hydroxyl group-containing starter (see Examples 2-4).

Although any desired amount of DMC compound can be used to make the foam-supported catalysts of the invention, it is generally preferred to include an amount of DMC compound within the range of about 1 to about 20 weight percent based on the amount of foam-supported catalyst produced. A more preferred range is from about 5 to about 15 weight percent.

After the foam is prepared, it is preferably vacuum dried to remove moisture and other volatile impurities. I surprisingly found that catalyst activity improves when a vacuum drying step is included in the catalyst preparation. The vacuum drying is preferably performed at a temperature within the range of about 20° C. to about 90° C., more preferably from about 30° C. to about 60° C., at a vacuum of less than about 100 mm Hg.

The invention includes a process for making a polyether polyol. This process comprises polymerizing an epoxide in the presence of the polyurethane foam-supported DMC catalyst of the invention. Preferred epoxides are ethylene oxide, propylene oxide, butene oxides, styrene oxide, and the like, and mixtures thereof. The process can be used to make random or block copolymers from the epoxides in the same manner as is used to make epoxide copolymers with unsupported DMC catalysts.

Other monomers that will copolymerize with an epoxide in the presence of a DMC compound can be included in the process of the invention to make modified polyether polyols. Any of the copolymers known in the art made using unsupported DMC catalysts can be made with the foam-supported catalysts of the invention. For example, epoxides copolymerize with oxetanes (as taught in U.S. Pat. Nos. 3,278,457 and 3,404,109) to give polyethers, or with anhydrides (as taught in U.S. Pat. Nos. 5,145,883 and 3,538,043) to give polyester or polyetherester polyols. The preparation of polyether, polyester, and polyetherester polyols using DMC catalysts is fully described, for example, in U.S. Pat. Nos. 5,223,583, 5,145,883, 4,472,560, 3,941,849, 3,900,518, 3,538,043, 3,404,109, 3,278,458, 3,278,457, and in J. L. Schuchardt and S. D. Harper, SPI Proceedings, 32nd Annual Polyurethane Tech./Mark. Conf. (1989) 360. The teachings of these references related to polyol synthesis using DMC catalysts are incorporated herein by reference in their entirety.

A solvent is optionally included in making polyether polyols by the process of the invention. Suitable solvents are those in which the epoxide and hydroxyl group-containing starter are soluble, and which do not deactivate the double metal cyanide catalyst. Preferred solvents include aliphatic and aromatic hydrocarbons, ethers, ketones, and esters. A solvent is not usually necessary, however, and it is often preferred for economic reasons to make the polyethers in the absence of a solvent.

A key advantage of the foam-supported catalysts of the invention is that they have high activity compared with unsupported powdered catalysts. Polymerization rates two or more times greater than the normal rate of polymerization with the same concentration of DMC compound are typical. A consequence of higher polymerization rates is that polyol producers can reduce the amount of relatively expensive DMC catalyst used in the process and save money. More active catalysts also permit the producer to reduce batch times and increase productivity.

Another advantage of the foam-supported catalysts of the invention for making polyether polyols is that they show a reduced induction period. Conventional unsupported DMC catalysts are not immediately active toward epoxide polymerization. Typically, a starter polyol, the catalyst, and a small amount of epoxide are combined and heated to the desired reaction temperature, and no epoxide polymerizes immediately. The polyol manufacturer must wait (usually for one to several hours) until the catalyst becomes active and the charged epoxide begins to react before additional epoxide can safely be continuously added to the polymerization reactor. The foam-supported catalysts are more rapidly activated than conventional powdered catalysts. This feature of the catalysts is an economic advantage because delays in adding the epoxide are reduced. The induction period can be eliminated by using an activated polyurethane foam-supported catalyst prepared as described earlier.

Another advantage of the foam-supported catalysts of the invention is that they can be isolated from the polyether polyol products by filtration, and can be reused to catalyze additional epoxide polymerizations. This is illustrated by Example 10 below. Most catalyst removal methods for DMC catalysts irreversibly deactivate the catalyst (see, for example, U.S. Pat. Nos. 5,144,093, 5,099,075, 4,987,271, 4,877,906, 4,721,818, and 4,355,188), so that reuse of the catalyst is not possible. The methods described in U.S. Pat. No. 5,010,047 can also be used to recover the supported catalysts of the invention from polyols.

The foam-supported catalysts of the invention can be used in a batch, continuous, or semi-continuous process. The foam can be used "as is," or it can be cut up, pulverized, or ground into small pieces prior to use as a catalyst. Preferably, the foam is reticulated, i.e., the foam is subjected to conditions that are effective to open a substantial proportion of the cells. One method of making a reticulated foam is to crush the foam soon after preparation to maximize the number of open cells in the foam, and to permit maximum air flow through the foam. The reticulated foam can then be used "as is" or it can be cut up. A cut up or pulverized foam is well-suited for use in a batch-type process.

A fixed-bed catalyst system suitable for a continuous process is conveniently made by foaming the DMC compound-containing polyurethane mixture in place in a column. Epoxide and starter polyol can then be passed through the column at the desired reaction temperature under conditions effective to produce a polymer product that has the desired molecular weight.

Polyether polyols made with the foam-supported catalysts of the invention contain an unusually low level of low molecular weight polyol impurities. When a powdered catalyst is used (glyme complexing agent), the polyol product typically contains up to about 5-10 weight percent of a low molecular weight polyol impurity, as is evident from gel-permeation chromatography analysis of the product. Surprisingly, polyols made from a foam-supported catalyst of the invention (in which glyme is used to make the powdered catalyst) do not contain detectable levels of low molecular weight polyol impurities.

The following examples merely illustrate the invention. Those skilled in the art will recognize many variations that are within the spirit of the invention and scope of the claims.

EXAMPLE 1 PREPARATION OF POLYURETHANE FOAM-SUPPORTED ZINC HEXACYANOCOBALTATE

A flexible, polyurethane foam is prepared according to the one-shot method. ARCOL 3520 polyol (3500 molecular weight, mixed EO-PO triol containing 10-15 wt. % EO recurring units, product of ARCO Chemical Company, 56.8 g) is blended with water (2.28 g), L-6202 surfactant (0.5 g, product of Dow Corning), A-1 amine catalyst (0.1 g, product of Air Products), A-33 catalyst (0.02 g, product of Air Products), T-12 catalyst (0.5 g, product of Air Products), and zinc hexacyanocobaltate powdered catalyst (10.0 g, prepared as described in U.S. Pat. No. 5,158,922 using glyme as a complexing agent). Toluene diisocyanate (80:20 mixture of 2,4- and 2,6-isomers, 29.8 g, 110 NCO index) is added in one portion to the B-side components, and the mixture is rapidly blended at room temperature. The mixture is poured into a box, where it rises and cures to form a cured polyurethane foam. The foam is cured at 110° C. for 30 min., and is cut into small pieces. The cut-up foam is dried in a vacuum oven at 50° C. for 90 min. to remove volatile materials. This dried, foam-supported catalyst is identified as Catalyst A.

Additional foam-supported catalyst is prepared as described above, but the vacuum drying step at 50° C. is omitted. This "non-dried" catalyst is designated as Catalyst B.

EXAMPLES 2-4 PREPARATION OF A POLYETHER POLYOL USING FOAM-SUPPORTED ZINC HEXACYANOCOBALTATE (CATALYST A: DRIED CATALYST)

A one-liter stainless-steel stirred reactor is charged with poly(oxypropylene) triol (700 mol. wt.) starter (50 g) and polyurethane foam-supported zinc hexacyanocobaltate catalyst (0.5-1 g, as prepared in Example 1, 110-222 ppm level in the finished polyol product). The mixture is stirred and stripped under vacuum to remove traces of water from the triol starter. Heptane (130 g) is added to the reactor, and the mixture is heated to 105° C. The reactor is pressurized to about 2 psi with nitrogen. Propylene oxide (15-20 g) is added to the reactor in one portion, and the reactor pressure is monitored carefully. Additional propylene oxide is not added until an accelerated pressure drop occurs in the reactor; the pressure drop is evidence that the catalyst has become activated. When catalyst activation is verified, the remaining propylene oxide (380-385 g) is added gradually over about 1-3 h at 105° C. at a constant pressure of about 25 psi. After propylene oxide addition is complete, the mixture is held at 105° C. until a constant pressure is observed. Residual unreacted monomer is then stripped under vacuum from the polyol product, and the polyol is cooled and recovered. The polymerization rates and induction periods observed for various catalyst concentrations of these dried, foam-supported catalysts appear in Table 1.

COMPARATIVE EXAMPLES 5-7 PREPARATION OF A POLYETHER POLYOL USING POWDERED ZINC HEXACYANOCOBALTATE

The procedure of Examples 2-4 is repeated, except that the catalyst used is an unsupported, powdered zinc hexacyanocobaltate catalyst prepared by the method of U.S. Pat. No. 5, 158,922 using glyme as a complexing agent. The catalyst is used at a 100-250 ppm level. The polymerization rates and induction periods observed at various catalyst concentrations of these powdered catalysts appear in Table 1.

The results of Examples 2-4 and Comparative Examples 5-7 show that the foam-supported zinc hexacyanocobaltate catalyst is more active and exhibits a shorter induction time than the powdered catalyst when each is used at about the same zinc hexacyanocobaltate concentration. For example, the foam-supported catalyst at only 110 ppm has comparable activity (3.4 g/min) and induction time (175 min) to the powdered catalyst at 250 ppm (activity=3.5 g/min, induction time=180 min).

EXAMPLES 8-9 PREPARATION OF A POLYETHER POLYOL USING FOAM-SUPPORTED ZINC HEXACYANOCOBALTATE EFFECT OF MOISTURE ON CATALYST ACTIVITY AND INDUCTION PERIOD (FOAM-SUPPORTED CATALYSTS)

The procedure of Examples 2-4 is followed with 2 g of foam-supported catalyst. In Example 8, the dried, foam-supported catalyst (Catalyst A) is used. Example 9 uses a foam-supported catalyst prepared without a vacuum drying step (Catalyst B).

When Catalyst A (dried) is used, the rate of propylene oxide polymerization is 13.3 g/min, and the induction period is 140 min. With Catalyst B (non-dried), the rate is 7.3 g/min, and the induction period is 160 min.

The results show that vacuum drying following preparation improves the foam-supported zinc hexacyanocobaltate catalyst.

EXAMPLE 10 RECOVERY AND REUSE OF FOAM-SUPPORTED ZINC HEXACYANOCOBALTATE CATALYST

A one-liter stainless-steel stirred reactor is charged with poly(oxypropylene) triol (700 mol. wt.) starter (50 g) and polyurethane foam-supported zinc hexacyanocobaltate catalyst (Catalyst B, 4 g, as prepared in Example 1,700 ppm level in the finished polyol product). The mixture is stirred and stripped under vacuum to remove traces of water from the triol starter. Heptane (130 g) is added to the reactor, and the mixture is heated to 105° C. The reactor is pressurized to about 6 psi with nitrogen. Propylene oxide (11 g) is added to the reactor in one portion, and the reactor pressure is monitored carefully. Additional propylene oxide is not added until an accelerated pressure drop occurs in the reactor; the pressure drop is evidence that the catalyst has become activated. When catalyst activation is verified, the remaining propylene oxide (389 g) is added gradually over about 1-3 h at 105° C. at a constant pressure of about 25 psi. After propylene oxide addition is complete, the mixture is held at 105° C. until a constant pressure is observed. Residual unreacted monomer is then stripped under vacuum from the polyol product, and the polyol is cooled and recovered. The rate of polymerization is 7.6 g/min. The resulting polyether polyol product has a hydroxyl number of 27.9 mg KOH/g and an unsaturation of 0.017 meq/g.

Following polymerization, the foam-supported catalyst is recovered from the mixture by filtration. The catalyst is washed with acetone and is dried. The recovered catalyst is used to catalyze a second polymerization of propylene oxide as described in this example. The rate of polymerization observed in the second run is 3.4 g/min. The polyether polyol product has a hydroxyl number of 28.3 mg KOH/g and an unsaturation of 0.019 meq/g.

                  TABLE 1                                                          ______________________________________                                         Polyol Synthesis with Foam-Supported and Powdered Zinc                         Hexacyanocobaltate Catalysts: Catalyst Activity                                and Induction Period                                                                                                Induction                                      Catalyst  Catalyst  Polymerization rate                                                                        Period                                    Ex # type      level (ppm)                                                                              (g/min)     (min)                                     ______________________________________                                         2    Foam-     110       3.4         175                                            supported                                                                 3              167       5.7         165                                       4              222       8.0         145                                       C5   Powdered  100       1.46        230                                       C6             130       1.78        175                                       C7             250       3.50        180                                       ______________________________________                                    

The preceding examples are meant as illustrations; the scope of the invention is defined by the following claims. 

I claim:
 1. A catalyst which comprises a polyurethane foam-supported double metal cyanide compound.
 2. The catalyst of claim 1 wherein the double metal cyanide compound is a zinc hexacyanocobaltate compound.
 3. The catalyst of claim 1 prepared by combining a polyol, a polyisocyanate, water, a surfactant, a foaming catalyst, and a double metal cyanide compound under conditions effective to produce a polyurethane foam-supported double metal cyanide compound.
 4. The catalyst of claim 1 wherein the double metal cyanide compound is present in an amount within the range of about 1 to about 20 weight percent based on the amount of catalyst.
 5. The catalyst of claim 1 which comprises a reticulated polyurethane foam-supported double metal cyanide compound.
 6. A process for making an activated catalyst, said process comprising:(a) preparing an activated double metal cyanide compound/starter mixture by exposing a double metal cyanide compound to an epoxide and a hydroxyl group-containing starter under conditions effective to activate at least a portion of the double metal cyanide compound; (b) isolating the activated double metal cyanide compound from the mixture; and (c) preparing a polyurethane foam from a polyol, a polyisocyanate, water, a surfactant, a foaming catalyst, and the activated double metal cyanide compound, wherein the resulting catalyst is an activated, polyurethane foam-supported double metal cyanide compound.
 7. The process of claim 6 wherein the double metal cyanide compound is a zinc hexacyanocobaltate.
 8. An activated, polyurethane foam-supported double metal cyanide compound made by the process of claim
 6. 9. A process for making an activated catalyst, said process comprising:(a) preparing an activated double metal cyanide compound/starter mixture by exposing a double metal cyanide compound to an epoxide and a hydroxyl group-containing starter under conditions effective to activate at least a portion of the double metal cyanide compound; and (b) preparing a polyurethane foam from a polyisocyanate, water, a surfactant, a foaming catalyst, the activated double metal cyanide compound/starter mixture, and optionally a polyol, wherein the resulting activated catalyst is an activated, polyurethane foam-supported double metal cyanide compound.
 10. A process which comprises reacting a polyol, a polyisocyanate, and water in the presence of a surfactant, a foaming catalyst, and a double metal cyanide compound under conditions effective to produce a polyurethane foam-supported double metal cyanide catalyst.
 11. The process of claim 10 wherein the double metal cyanide compound is a zinc hexacyanocobaltate.
 12. The process of claim 10 which comprises reacting the polyol, polyisocyanate, and water in the presence of from about 1 to about 20 weight percent, based on the amount of polyurethane foam-supported catalyst, of the double metal cyanide compound.
 13. The process of claim 10 which further comprises subjecting the resulting polyurethane foam-supported double metal cyanide catalyst to conditions effective to produce a reticulated foam.
 14. The process of claim 10 which further comprises drying the resulting polyurethane foam-supported double metal cyanide catalyst under vacuum. 